产品用途：用途：对耐摩擦磨损性能有要求的部件。
备注说明：特性：耐摩擦摩损型。
LS-1250 物性表
| 吸水率 (23°C水中24小时) | 0.17 | % | ASTM D-570 |
| 比重 | 1.26 | ASTM D-792 | |
| 阻燃性 | UL 94 | ||
| (厚度1.47mm) | 94V-2 | ||
| (厚度3.05mm) | 94V-1 | ||
| 透光率 (厚度3mm) | 半透明 | % | ASTM D-1003 |
| 弯曲强度 | 78(800) | Mpa(kgf/cm) | ASTM D-790 |
| 拉伸率 | ASTM D-638 | ||
| 6 | |||
| 110 | |||
| 耐冲击强度值 (艾氏.带缺口厚度6.4mm) | 120(12) | j/m(kgf·cm/cm) | ASTM D-256 |
| 拉伸模量 | 2300(23500) | Mpa(kgf/cm) | ASTM D-638 |
| 洛氏硬度 | 67 | M标度 | ASTM D-785 |
| 耐冲击强度值 (艾氏.带缺口厚度3.2mm) | 290(30) | j/m(kgf·cm/cm) | ASTM D-256 |
| 弯曲模量 | 2110(21500) | Mpa(kgf/cm) | ASTM D-790 |
| 压缩强度 | 73(740) | Mpa(kgf/cm) | ASTM D-695 |
| 拉伸强度 | ASTM D-638 | ||
| 55(560) | Mpa(kgf/cm) | ||
| 51(520) | Mpa(kgf/cm) | ||
| 绝缘破坏强度 (快速加压值厚度1.6mm) | 30 | KV/mm | ASTM D-149 |