CM1011G-45
PA6 | 聚已内酰胺#尼龙6日本东丽规格级别：注塑
CM1011G-45 物性表
基本性能额定值单位测试方法
| 吸水率 |
|
| ASTM D-570 |
| (23℃.24hr) | Dry|1.9%Water0.9|- | % |
|
| (23℃) | Dry|1.9%Water5.3|- | % |
|
物理性能额定值单位测试方法
| 比重 | Dry|1.9%Water1.50|- |
| ASTM D-792 |
机械性能额定值单位测试方法
| 断裂伸长率 (-40℃) | Dry|1.9%Water4.5|4.5 | % | ASTM D-638 |
| 弯曲模量 (23℃) | Dry|1.9%Water12.0|7.1 | GPa | ASTM D-790 |
| IZOD缺口冲击强度 (-40℃) | Dry|1.9%Water125|145 | J/m | ASTM D-256 |
| 弯曲模量 (80℃) | Dry|1.9%Water6.2|4.4 | GPa | ASTM D-790 |
| 拉伸屈服强度 (23℃) | Dry|1.9%Water205|130 | MPa | ASTM D-638 |
| 弯曲模量 (-40℃) | Dry|1.9%Water14.0|12.5 | GPa | ASTM D-790 |
| 弯曲强度 (23℃) | Dry|1.9%Water290|180 | MPa | ASTM D-790 |
| 断裂伸长率 (23℃) | Dry|1.9%Water5.0|5.0 | % | ASTM D-638 |
| 拉伸屈服强度 (80℃) | Dry|1.9%Water120|85 | MPa | ASTM D-638 |
| IZOD无缺口冲击强度 (23℃) | Dry|1.9%Water100|120 | KJ/m | ASTM D-256 |
| 弯曲强度 (-40℃) | Dry|1.9%Water330|280 | MPa | ASTM D-790 |
| IZOD缺口冲击强度 (23℃) | Dry|1.9%Water155|195 | J/m | ASTM D-256 |
| 抗压强度 |
|
| ASTM D-695 |
| (-40℃) | Dry|1.9%Water260|220 | MPa |
|
| (23℃) | Dry|1.9%Water190|120 | MPa |
|
| (80℃) | Dry|1.9%Water100|70 | MPa |
|
| 剪切强度 (23℃) | Dry|1.9%Water95|75 | MPa | ASTM D-732 |
| 断裂伸长率 (80℃) | Dry|1.9%Water8.0|8.0 | % | ASTM D-638 |
| 弯曲强度 (80℃) | Dry|1.9%Water160|110 | MPa | ASTM D-790 |
| 洛氏硬度 (23℃) | Dry|1.9%WaterR121,M95|- | R Scale | ASTM D-785 |
| IZOD无缺口冲击强度 (-40℃) | Dry|1.9%Water90|95 | KJ/m | ASTM D-256 |
| 拉伸屈服强度 (-40℃) | Dry|1.9%Water290|250 | MPa | ASTM D-638 |
热性能额定值单位测试方法
| 热导率 | Dry|1.9%Water0.40|- | W/m℃ |
|
| 线性热膨胀系数 | Dry|1.9%Water2-3|- | 10-5/℃ | ASTM D-696 |
| 比热 | Dry|1.9%Water1.4|- | J/p℃ |
|
| 熔点 | Dry|1.9%Water225|- | ℃ | DSC |
| 热变形温度 |
|
| ASTM D-648 |
| (0.46MPa) | Dry|1.9%Water225|- | ℃ |
|
| (1.86MPa) | Dry|1.9%Water215|- | ℃ |
|
其它性能额定值单位测试方法
| 加强材料 | Dry|1.9%Water45|45 | WT% |
|
核心提示：PA6 1011G-45，GF增强PA6